World’s fastest directly modulated laser exceeding 100-GHz bandwidth

(Press Release)

October 20, 2020

NTT Corporation
Tokyo Institute of Technology

World’s fastest directly modulated laser exceeding 100-GHz bandwidth
~Membrane laser on silicon carbide substrate achieves low power consumption

Nippon Telegraph and Telephone Corporation (Head Office: Chiyoda Ward, Tokyo; President and Representative Director: Jun Sawada, NTT), in collaboration with Fumio Koyama, professor at the Laboratory for Future Interdisciplinary Research of Science and Technology, Tokyo Institute of Technology (Meguro-ku, Tokyo, President: Kazuya MASU), has developed a membrane laser*1 that uses an indium-phosphorus compound semiconductor*2 on a silicon carbide substrate*3 with high thermal conductivity. This laser, the world’s first directly modulated laser with a 3-dB bandwidth*4 exceeding 100 GHz, can transmit at 256 gigabits (256 billion bits) per second over a distance of 2 km.
Directly modulated lasers are now widely used in data centers*5, but their modulation speed is limited, which has been a problem for further increasing in transmission capacity. These results will enable us to respond to the expected increase in traffic with a low-cost and low-power-consumption solution and will contribute to the realization of a high-capacity optical transmission infrastructure that supports NTT’s IOWN*6 concept.
This research was reported in Nature Photonics on October 19, 2020.

Background to Research

Data traffic will continue to increase in the future, especially in data centers where data is concentrated. Therefore, it is essential to increase the capacity of optical interconnections*7 that connect servers. Moreover, the increase in power consumption in data centers must be suppressed, so it is important to reduce the power consumption of optical interconnects. Currently, directly modulated lasers are widely used in data centers because of their low power consumption and low cost. However, since they use intensity modulation, in which the light (photons*8) output varies in proportion to the current (carrier*9) injected into the laser, their modulation speed is limited by the relaxation oscillation frequency*10, which is the interaction between carriers and photons. Figure 1 shows the evolution of the 3-dB bandwidth for directly modulated lasers over the last 30 years. In the 1990s, the performance of the laser active layer*11 was improved, resulting in a 3-dB bandwidth of about 30 GHz, but no significant progress has been made since then.
Since further improving the performance of the active layer is considered to be difficult, photon-photon resonance has attracted attention as an additional speed-up method. In this method, when the frequency detuning between the lasing mode*12 and the adjacent cavity mode*13 coincides with a specific modulation frequency, the sideband*14 generated by the intensity modulation is enhanced. Figure 2 shows the change in the 3-dB bandwidth when photon-photon resonance is applied. Up to now, a 3-dB bandwidth of 55 GHz has been achieved, and PAM4 signal modulations*15 at 112 gigabits per second have been demonstrated.
Although it is possible to increase the response of a specific frequency by adjusting the detuning, it is necessary to have a flat frequency response characteristic from a low-frequency region to a high-frequency region for further speed-up. For this purpose, it is important to increase the relaxation oscillation frequency and prevent a large drop between the relaxation oscillation frequency and the photon-photon resonance frequency.

More:  Neutron energy dependence of semiconductor soft errors was successfully measured for the first time

Research Results

To increase the relaxation oscillation frequency, NTT researchers focused on the optical confinement factor of the active region and developed a membrane laser on a silicon (Si) substrate with a thermal oxide film (SiO2). Membrane lasers have a large optical confinement factor in the active region and are compact, making it possible to realize directly modulated lasers with low power consumption. On the other hand, since the device is fabricated on a low-thermal-conductivity SiO2 layer, the temperature increase in the active layer due to current injection is large, and even if the current is increased, the relaxation oscillation frequency saturates at about 20 GHz due to saturation of the differential gain.
To suppress the increase in the active region temperature, we fabricated an indium-phosphorus (InP) based membrane laser on a silicon carbide (SiC) substrate (Fig. 3), which has a thermal conductivity approximately 500 times higher than that of SiO2. Since SiC has a lower refractive index than InP, the optical confinement factor is almost the same as that of the device on SiO2. The device was fabricated by direct bonding with ultrathin (40 nanometers) SiO2 between the InP and SiC substrate. Assuming a 100-mW heat source, the temperature increase in the active region of a membrane laser with an active layer length of 50 micrometers was significantly reduced from 130.9 to 16.8℃ when the SiO2 thickness was reduced from 2 micrometers to 40 nanometers (Fig. 4). The current at which the relaxation frequency reaches its maximum was 5.5 mA for the device fabricated on SiO2/Si substrate. In contrast, with the device fabricated on SiC substrate, we were able to increase the current to 30 mA and obtain the world’s highest relaxation frequency of 42 GHz and 3-dB band of 60 GHz (Fig. 5).
In addition, using optical feedback from the end facet of the output waveguide, we designed a device in which photon-photon resonance occurs at around 95 GHz. As a result, we obtained a 3-dB bandwidth of 108 GHz (Fig. 6) and succeeded in generating a 256 gigabit (256 billion bit) PAM4 signal and transmitting it over a distance of 2 km (Fig. 7).

Future Developments

The future will see the development of transmitters capable of handling the next generation of Ethernet standards with transmission capacity exceeding 1 terabit with four or eight arrays. The simultaneous achievement of low power consumption is expected to suppress increases in the power consumption of data centers and supercomputers due to the anticipated increase in data volume.

More:  NTT named as a leader in IDC MarketScape for Worldwide Managed Security Services 2020

Technical Points

1.Membrane lasers on SiC substrate

As shown in Fig. 3, the membrane laser is a laser with total thickness of about 300 nm (1/10 that of conventional lasers) made on a low-refractive-index material. The active region is embedded in the InP layer, and a lateral current injection structure is formed. Since the membrane laser is sandwiched between low-refractive-index layers, light (photons) generated in the active region is strongly confined in it. In addition to this, since the injected carriers are also tightly confined in the active layer, low power consumption and high-speed modulation of direct modulation lasers can be expected. Figure 8 shows the optical mode field in membrane lasers on SiO2 and SiC. As shown in the figure, although SiC has about 500 times the thermal conductivity of SiO2, the optical confinement is similar.

2.Fabrication Method

SiC and InP are directly bonded to SiO2 using oxygen plasma. Although SiO2 provides good bonding strength, it is important to make it as thin as possible due to its low thermal conductivity. To prevent peeling of the film due to out-gas generated when the temperature rises after bonding, we succeeded in forming a groove in the substrate.
Figure 9 shows the fabrication process. First, the InP substrate is removed after direct bonding (a). Then, the active layer in the core region of the laser is left, and the active layer is etched away to the lower InP layer in other regions (b). InP is selectively regrown on the surface where the InP layer is exposed. This embeds the active layer into the InP layer (c). The device is then fabricated by selectively forming doping regions, gratings, and electrodes (d).

3.Design of cavity photon lifetime

When the relaxation oscillation frequency increases, the frequency response of the directly modulated laser is limited by the photon lifetime–the time that photons are confined in the cavity–and by the nonlinear saturation of the gain of the active layer. In this experiment, we focused on the photon lifetime. Figure 10 shows calculated frequency response characteristics when the photon lifetime in the cavity is changed. In the calculation, the relaxation oscillation frequency was kept constant at 40 GHz. As shown in the figure, the 3-dB bandwidth can be maximized by setting the photon lifetime at around one picosecond.